polyurethane paints

pu semigloss (pigmented)

PU SEMIGLOSS (PIGMENTED) is a polyurethane material based on saturated polyester resin. It is formulated to give maximum opacity, thanks to the high quality of raw material. Furthermore, PU SEMIGLOSS (PIGMENTED) is resistant to extreme weather with no – yellowing effect, resistant to abrasion and provides a very smooth finish.

Highly recommended to all woodworks, furniture such as beds, cabinets, chairs, sofas, doors, and frames, turned pieces and the likes.

Appearance – Transparent Liquid

Colour – As per RAL/NCS/APS

Specific Gravity (20ºC) – 1.23 +/- 0.2 kg/L

Viscosity(25ºC, FC#4) – 40 – 60 sec.

Flash Point – 21ºC

Non-Volatile(Wt.%) – 50 – 65

Gloss (600) – 40 – 60

Application Condition – Air Temperature 5 – 35ºC, Relative Humidity Max. 85%

Application Method – Brush, Spray or Roller

Recommended Catalyst – Catalyst #013

Thinner – PU Thinner#105/205

Mixing ratio/Dilution Ratio – (FC#4 ,13-15 sec.)

Base – 100

Cat. – 50

Thinner – 25-30

Pot life (20ºC) – 5 – 6 hours

Drying Time – Dust-free 15 – 17 min., To touch 45 – 60 min., To Recoat 2 – 3 hours, Hard 24 – 36 hours

Coating Rate – 6 – 8 m2/L

Basecoat – PU #153 Plastofil #350

  • The surface to be top coated should be primed with either polyurethane primer or polyester primer white.
  • It should be cleaned, well-sanded and free from dust, oil, water, and other contaminants to ensure a long-lasting effect.
  • For cracks, crates and nail holes, it is advisable to fill with either Putty filler, Putty white #2185 or Polyester putty.
  • Apply 1 – 2 coats of PU SEMIGLOSS (PIGMENTED) horizontally and vertically.
  • One coat may be sufficient for an ordinary finish, however; one additional coat can be applied wet on wet if necessary. Light sanding with 400-600 grit sandpaper is recommended before subsequent coats when recoating time exceeds 3 hrs.
brush-product