polyurethane paints

pu semigloss #1070 white

PU SEMIGLOSS #1070 WHITE is a polyurethane material based on saturated polyester resin. It is formulated to give maximum whiteness, thanks to the high quality of raw material. Furthermore, PU SEMIGLOSS #1070 WHITE is resistant to both extreme weather with no – yellowing effect, resistant to abrasion and provides a very smooth finish.

Highly recommended to all woodworks, furniture such as beds, cabinets, chairs, sofas, doors, and frames, turned pieces and the likes.

Appearance – Semi-gloss

Colour – White

Specific Gravity – 1.23 +/- 0.2 kg/L

Viscosity – 40 – 60” FC # 4 @ 25ºC

Flash Point – 21ºC

Non-volatile – 63%

Gloss (60ºC) – 40 – 60

Application Condition – Air temperature 5 – 35ºC, Relative Humidity 85% max.

Application Method – Auto or Conventional Spray

Recommended Catalyst – Catalyst #013

Thinner – Thinner #105 (Standard), Thinner #205 (Summer)

Mixing Ratio – Base 100, Cat. 50

Thinner – 20-25

Pot Life – 3 – 4 hours @ 25ºC

Coating Rate – 6 – 8 m2/L

Basecoat – PU Primer #153, Plastofil #350

  • The surface to be top coated should be primed with either polyurethane primer or polyester primer white.
  • It should be cleaned, well-sanded and free from dust, oil, water, and other contaminants to ensure a long-lasting effect.
  • For cracks, crates and nail holes, it is advisable to fill with either Putty filler, Putty white #2185 or Polyester putty.
  • Apply 1 – 2 coats of PU SEMIGLOSS #1070 WHITE horizontally and vertically.
  • One coat may be sufficient for an ordinary finish, however; one additional coat can be applied wet on wet if necessary. Light sanding with 400-600 grit sandpaper is recommended before subsequent coats when recoating time exceeds 3 hrs.