Polyurethane paints

PU hi-gloss #2250 black

PU HI-GLOSS #2250 BLACK is a polyurethane material based on saturated polyester resin.  It is formulated to give a maximum gloss, thanks for the high quality of raw material.  Furthermore, PU HI-GLOSS #2250 BLACK is resistant to both extreme weather with no-yellowing effect, resistant abrasion and provides a very smooth and glossy finish.

Highly recommended to all woodworks, furniture such as beds, cabinets, chairs, sofas, doors and frames, turned pieces and the likes.
The surface to be top coated should be primed with either Polyurethane Primer or Polyester Primer White.
It should be cleaned, well-sanded and free from dust, oil, water and other contaminants to ensure long lasting effect.
To obtain a smooth finish, ensure that the basecoat is sufficient to avoid uneven and irregular surface.
For cracks, crates and nail holes, it is advisable to fill with either Putty Filler. NC Putty #2185 White or Polyester Putty.
Apply 1-2 coats of PU HI-GLOSS #2250 BLACK horizontally and vertically.

Appearance – Liquid Pigmented

Colour – Black

Specific Weight – 1.05 kg/L

Viscosity (25°C) – 25 – 30” FC#4

Flash Point – 21°C

Non-Volatile – 45%

VOC Content – 535 g/L

Gloss (60%) >95

Application Condition
Air Temperature 5 -35°C
Relative Humidity 85% max.

Application Method – Conventional or Automatic Spraying

Recommended Catalyst – Catalyst #016

Mixing/Dilution Ratio (FC#4 @ 13-15 sec.)
Base 100
Cat. 50
Thinner 15-20

Pot Life (25°C) – 3 – 4 hrs.

Drying Time (25°C)
Dust Free 20 – 25 mins.
To Touch 45 – 60 mins.
To Recoat 2 – 3 hrs.
Hard Dry 24 – 36 hrs.

Coating Rate – 7 – 9 m2/L

Pencil Hardness – H -2H

One coat may be sufficient for ordinary finish. However, one additional coat can be applied wet on wet if necessary. Light sanding with 400-600 grit sand paper is recommended before subsequent coats when recoating time exceeds 3 hrs.

Recommended Basecoat – PU Primer White or Plastofil #350 White