Acrylic based paints
acrylic sealer lv/081
ACRYLIC SEALER LV/081 is based on acrylic resin for non-yellowing basecoat. It is developed to provide a good covering, good sanding ability and preserves natural colour of the wood. It is weather resistant, unaffected by humidity, heat and sunlight. ACRYIC SEALER LV/081 meets the VOC content limit of Annex ll, Phase ll, Table A of European Directive 2004/42/EC:2004.
Best recommended for furniture, tables, chair, doors and frames, outdoors furniture and external wood works.
Appearance – Opaque
Specific Gravity – 0.980 g/L
Viscosity @ 250C – 60” FC # 4
Flash Point – 230C
Solid Content (Wt.) – 40
Application Condition
Air Temperature 5
Relative Humidity 350C
Application Method – Brush, Roller, Spray
Catalyst – Catalyst LV/26
Thinner – PU Thinner #105/205
Mixing/Dilution Ratio (13-15” FC # 4)
Base 100
Hardener 20
Thinner 25-30
Drying Time
Dust Free 20 – 30 min.
To Touch 35 – 45 min
To Recoat 2 – 3 hours
Hard 24 – 36 hours
Coverage 5-7 m2/L (120 gms/m2)
Recoating
Minimum 30 min-max 3 hrs. medium sanding with 240-360 mesh sand paper is recommended before subsequent coat is needed.
The mixture ready for use, can be applied by brush, roller or spray. Surface to be painted must be free of dirt and other contaminants. In the remaking of old woods, it is imperative to remove traces of wax, dirt and other oily matter to ensure a perfect adhesion of paint. Apply 1 – 2 coats of Acrylic Sealer TA/061.
Mixing ration should be correctly observed.
Paint should be used within the pot life after components have been mixed together.
Pot life decreases at high temperature.
Bubbling due to excessive coatings within relatively short time is likely to occur in summer. 1-2 thin initial coat and longer recoating interval (50-60 min) eliminates bubbling.
Never leave drums of catalyst open.
Paint should be used within the pot life after components have been mixed together.
Pot life decreases at high temperature.
Bubbling due to excessive coatings within relatively short time is likely to occur in summer. 1-2 thin initial coat and longer recoating interval (50-60 min) eliminates bubbling.
Never leave drums of catalyst open.