PU gloss #2150 black
PU GLOSS#2150 BLACK is a polyurethane material based on saturated polyester resin and selected pigment. It is formulated to give maximum gloss and high jetness, thanks for the high quality of raw material. Furthermore, PU GLOSS #2150 BLACK is resistant to both extreme weather with non-yellowing effect, resistant to abrasion and provides a very smooth and glossy finish.
Appearance – Liquid Pigmented
Colour – Black
Specific Weight – 1.05 kg/L
Viscosity (25°C) – 25 – 30” FC#4
Flash Point – 21°C
Non-Volatile – 50%
VOC Content – 535 g/L
Gloss (60%) >95
Application Condition
Air Temperature 5 -35°C
Relative Humidity 85% max.
Application Method – Conventional or Automatic Spraying
Recommended Catalyst – Catalyst #016
Thinner – 105/ 205
Mixing/Dilution Ratio (FC#4 @ 13-15 sec.)
Base 100
Cat. 50
Thinner 25-20
Pot Life (25°C) – 3 – 4 hrs.
Drying Time (25°C)
Dust Free 20 – 25 mins.
To Touch 45 – 60 mins.
To Recoat 2 – 3 hrs.
Hard Dry 24 – 36 hrs.
Coating Rate – 7 – 9 m2/L
Pencil Hardness – H -2H
Recoating
One coat may be sufficient for ordinary finish. However, one additional coat can be applied wet on wet if necessary. Light sanding with 400-600 grit sand paper is recommended before subsequent coats when recoating time exceeds 3 hrs.
The surface to be top coated should be primed with either Polyurethane Primer or Polyester Primer White.
It should be cleaned, well-sanded and free from dust, oil, water and other contaminants to ensure long lasting effect.
To obtain a smooth finish, ensure that the basecoat is sufficient to avoid uneven and irregular surface.
For cracks, crates and nail holes, it is advisable to fill with either Putty Filler. NC Putty #2185 White or Polyester Putty.
Apply 1-2 coats of PU GLOSS #2150 BLACK horizontally and vertically.